| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | n.a. |
| Density | g mL-1 | 1.30 |
| Coefficient of Thermal Expansion | cm / (cm °C) x 10-5 | 4.0 |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa | °C | |
| Thermal Conductivity | W / mK | 0.28 |
| Rockwell Hardness, A Scale (Shore D) | n/a | |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 73 |
| Tensile Strength, Break at 23 C | MPa | 73 |
| Elongation, Yield | % | 5 |
| Elongation, Break | % | 5 |
| Tensile Modulus at 23 C | MPa | 4100 |
| Flexural Strength, Yield | MPa | 116 |
| Flexural Modulus | MPa | 3300 |
| Compressive Strength, 1% - 2% | MPa | 23 - 41 |
| Charpy Impact Strength | kJ/m2 | 37 |
| Izod Unnotched | J / m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm x 1014 | ||
| Dielectric Strength | V/mm x 104 | ||
| Dielectric Constant @ 1 MHz | n/a | ||
| Dissipation Factor @ 1 MHz | n/a, x 10-4 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
| Mold Shrinkage | % | ||
| Continuous Service Temperature | °C | 85 | |
| Water Absorption, 24 hr. Immersion | % | 0.01 - 0.02 |